Bronze Bushing #500 SWP Oilless Thin Wear Plate

Brass 500 SWP Wear Bronze Plate With Graphite Embedded

 

NO.	DIN	Material No.	Designation	ASTM Standard	Proportional	Density (g/cm³)	0.2% Strain (MPa)	Tensile Strength (MPa)	Strain (%)	E-modulus (MPa)	Hardness (HB)	Applications
1	1705	2.1090.01	CuSn7ZnPb	B 584	Cu 81 - 85, Sn 6 - 8, Zn 3 - 5, Pb 5 - 7	8.8	120	240	15	106,000	65	Widely utilized in automotive, and marine engineering for components requiring good strength and corrosion resistance. Recognized internationally for versatility and performance.
		2.1090.03	CuSn7ZnPb	B 271	Cu 81 - 85, Sn 6.3 - 7.5, Zn 2 - 4, Pb 6 - 8	8.8	130	270	13	106,000	75
		2.1090.04	CuSn7ZnPb	B 505	Cu 81 - 85, Sn 6.3 - 7.5, Zn 2 - 4, Pb 6 - 8	8.8	120	270	16	106,000	70
2	1705	2.1061.01	CuSn12Pb	Not yet standardized	Cu 84 - 87, Sn 11 - 13, Pb 1 - 2	8.7	140	260	10	112,000	80	Commonly used in manufacturing bearings, bushings, and components that require high load capacity and wear resistance, especially in marine and industrial applications.
		2.1061.03	CuSn12Pb	Not yet standardized	Cu 85 - 88, Sn 10 - 12, Pb 1 - 1.5	8.7	150	280	5	112,000	90
		2.1061.04	CuSn12Pb	B 505	Cu 85 - 88, Sn 10 - 12, Pb 1 - 1.5	8.7	140	280	7	112,000	85
3	1714	2.0975.01	CuAl10Ni	B 584	Cu min. 75, Al 8.5 - 11.0, Ni 4.0 - 6.5, Fe 3.5 - 5.5	7.6	270	600	12	122,000	140	Used in marine, and heavy machinery for manufacturing bearings and components requiring high strength and durability. Known for extreme loads and high corrosive environments.
		2.0975.02	CuAl10Ni	B 30	Cu min. 75, Al 8.5 - 11.0, Ni 4.0 - 6.5, Fe 3.5 - 5.5	7.6	300	600	14	122,000	150
		2.0975.03	CuAl10Ni	B 271	Cu min. 75, Al 8.5 - 11.0, Ni 4.0 - 6.5, Fe 3.5 - 5.5	7.6	300	700	13	122,000	160
		2.0975.04	CuAl10Ni	B 505	Cu min. 75, Al 8.5 - 11.0, Ni 4.0 - 6.5, Fe 3.5 - 5.5	7.6	300	700	13	122,000	160
4	1709	2.0598.01	CuZn25Al5	B 584	Cu 60 - 67, Al 3 - 7, Fe 1.5 - 4, Mn 2.5 - 5, Zn rest	8.2	450	750	8	115,000	180	Used in heavy-duty bearings, hydraulic components, and marine hardware. Designed for high loads and resistance to corrosive attack.
		2.0598.02	CuZn25Al5	B 30	Cu 60 - 66, Al 5 - 7.5, Fe 2 - 4, Mn 2.5 - 5, Zn 22 - 28	8.2	480	750	8	115,000	180
		2.0598.03	CuZn25Al5	B 271	Cu 60 - 66, Al 5 - 7.5, Fe 2 - 4, Mn 2.5 - 5, Zn 22 - 28	8.2	480	750	5	115,000	190
5	1705	2.1052.01	CuSn12	Not yet standardized	Cu 84 - 88, Sn 11 - 13, Pb 1, Ni 2.0, Sb 0.2, P 0.2	8.6	140	260	12	110,000	80	Commonly used in manufacturing bearings, gears, and components requiring high wear resistance. Known for good machinability and corrosion resistance, particularly in seawater environments. All rights to the listed content are reserved by /
		2.1052.03	CuSn12	Not yet standardized	Cu 85 - 88, Sn 10 - 12, Pb 1 - 1.5	8.6	150	280	8	110,000	90
		2.1052.04	CuSn12	Not yet standardized	Cu 85 - 88, Sn 10 - 12, Pb 1 - 1.5	8.7	140	280	8	110,000	95
Note: Delivery form codes: .01 = sand casting, .02 = gravity casting, .03 = centrifugal casting, .04 = continuous casting.

Standard No	W	L	a	b	Sketch
SWP Wear Plate -18*50	18	50	-	20	A
SWP Wear Plate -18*75		75		45
SWP Wear Plate -18*100		100		70
SWP Wear Plate -18*150		150		60	B
SWP Wear Plate-28*50	28	50	-	20	A
SWP Wear Plate -28*75		75		45
SWP Wear Plate -28*100		100		70
SWP Wear Plate -28*150		150		60	B
SWP Wear Plate-38*50	38	50	-	20	A
SWP Wear Plate -38*75		75		45
SWP Wear Plate-38*100		100		70
SWP Wear Plate -38*150		150		60	B
SWP Wear Plate -48*75	48	75	-	45	A
SWP Wear Plate -48*100		100		70
SWP Wear Plate -48*125		125		95
SWP Wear Plate -48*150		150		60	B
SWP Wear Plate -75*75	75	75	45	45	C
SWP Wear Plate -75*100		100		70
SWP Wear Plate-75*125		125		95
SWP Wear Plate -75*150		150		60	D
SWP Wear Plate -100*100	100	100	70	70	C
SWP Wear Plate -100*125		125		95
SWP Wear Plate -100*150		150		60	D

 

Brass Plate Properties: "SOLP"

 

Sliding speed v:	30 m/min
Base Material:	Special Brass (SO#50SP2)
Self-lubricating:	Yes
Lubricant:	Graphite
Surface Pressure P:	100 N/mm²
P*v-value:	200 N/mm² x m/min
Operating temperature:	-50°C / +200°C (max. 300°C)
Friction coefficient:	0,07